Tungsten Carbide Wear Plate — Wear Form(1/2)

Generally, the medium of tungsten carbide wear plate is concrete, which is composed of cement, water, fine coarse aggregate and other additives and the hardness index converted to a Rockwell hardness of between about HRC40-50. In the process, the main wear forms can be divided into two types, one is in the process of cutting ring reversal, wear plate and floating cutting ring contacts and has grain wear and erosion; the other is in the process of inhaling or pumping, the internal hole of wear plate has low stress wear and erosion.

After concrete pump working for some time, there is a gap between tungsten carbide wear plate and cutting ring. Theoretically, grinding compounds friction and grinding compounds wear of the sliding contact surfaces are generally the form of typical wear. Both wear plate and cutting ring are tungsten carbide and form a pair of friction, the floating cutting ring swings back and forth on tungsten carbide wear plate quickly. Both of them form grain wear by surface contact constantly.

In addition, there are still ore, quartz sand and some other hard particles, and the concrete also belongs to corrosive medium, which will further exacerbate the grinding compounds wear of tungsten carbide wear plate. At present, with the increasing height of the building, pumping height and pressure is also rising, which for carbide glasses plate and cutting ring put forward higher requirements. As time goes by, it will gradually appear larger gaps or partial abrasion between the cutting ring and the wear plate, and leading to failure of the wear plate finally.

• < Prev
• Next >