Nanostructured Composite using （APT) and Al Powder Mixture

W–Al₂O₃ nanostructured composite has been produced by mechanical milling of ammonium paratungstate (APT) and Al powder mixture at room temperature. The milled products have been characterized by X-ray diffraction (XRD), and scanning electron microscopy (SEM) equipped with energy dispersive spectrometry (EDS). The XRD and EDS results confirmed that direct reduction of APT to α-W took place after 25 min milling. It was observed that α→β phase transition took place after 24h mechanical milling. SEM micrographs showed that alumina matrix composite reinforced with W could be obtained by one step MSR (mechanically induced self-propagation reaction) process. X-ray diffraction peak broadening equation confirmed that the mean grain size of these particles was in nanometer range which gradually decreased with increasing the milling time.

Tungsten Powder Manufacturer & Supplier: Chinatungsten Online - http://www.tungsten-powder.com
Tel.: 86 592 5129696; Fax: 86 592 5129797
Email: sales@chinatungsten.com
Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn

• < Prev
• Next >