Cesium Tungsten Oxide Applied for Sun Protection Glass

Cesium tungsten oxide is often applied for preparing sun protection glass in the form of heat insulation coating film with excellent near-infrared absorption properties and high transparency. Well, do you know how to prepare the functional material - Cs0.33WO3 particles?

More details, please visit:
http://cesium-tungsten-bronze.com/index.html

Preparation of Cs0.33WO3 Particles for Sun Protection Glass

Using sodium tungstate and cesium carbonate as raw materials, cesium tungsten oxide (Cs0.33WO3) powder can be synthesized by hydrothermal reaction at 190 °C with citric acid as the reducing agent. Firstly, a precursor solution with n (Cs): n (W) = 0.33:1 containing appropriate citric acid was prepared using sodium tungstate and cesium carbonate as raw materials. Then the precursor solution was transferred into a Teflon-lined autoclave and heated at 190 °C for 3 days, and pure Cs0.33WO3 powders could be finally obtained after being washed with water and ethanol three times respectively and dried at 80 °C overnight. Finally, the as-prepared Cs0.33WO3 powders were annealed under N2 atmosphere at 500 °C for 2 h.

• < Prev
• Next >