4. The overhaul of tungsten contacts ablation on tungsten contact spring arm in distributor

If there is no spring balance, you can check tungsten contacts gap firstly. If the gap is greater than the 0.37mm, that is normal, then the tungsten contacts are closed, and then hand struck tungsten contacts to test fire, if there is a strong high voltage spark, then the tungsten contact spring arm is too soft.

If you have a spring balance, then: You can use spring balance to hook one end of the active tungsten contact arm, when the contact is opened, if the reading on the spring balance does not meet the spring force standard of tungsten contact of the car model, you should replace it, On the other hand, you do not need to replace it.

5. The overhaul of capacitor ground

You must fasten the capacitor case and tighten the wire point in order.




Tungsten Metals Manufacturer & Supplier: Chinatungsten Online - http://www.tungsten.com.cn
 Tel.: 86 592 5129696; Fax: 86 592 5129797
 Email: sales@chinatungsten.com
 Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
 Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
 Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn

2. The overhaul of tungsten contacts ablation on riveting loose or bracket set screw loose.
First, open the distributor cap, the first is visual inspection of the condition of tungsten rivet and contacts bracket set screw loose situation, and then, and then pull the two tungsten contacts back and forth. If the tungsten contacts are loose, then: you should remove tungsten contacts, re-riveting, to make it no loose, or replacement tungsten contacts directly.
If the tungsten contacts bracket set screw is loose, then tighten it.

3. The overhaul of the skew and offset condition of contact surface.
First, open the distributor cap, the first is visual inspection of the offset, skew situation.
If the contact surface offset, then: You can adjust the gasket of active tungsten contact arm.
If the contact surface of tungsten contacts has skew or excursion, then: You can use pliers to twist tungsten contacts frame to correct.

Tungsten Metals Manufacturer & Supplier: Chinatungsten Online - http://www.tungsten.com.cn
 Tel.: 86 592 5129696; Fax: 86 592 5129797
 Email: sales@chinatungsten.com
 Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
 Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
 Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn

1. The overhaul of tungsten contacts gap in distributor.

Open the lid of the distributor, shake and rotate the engine, so that tungsten contacts of the distributor is in good state, then, check the gap among tungsten contacts, to see whether it is less than 0.37mm, if less than 0.37mm, we need to check the extent of tungsten contacts ablation, otherwise, you do not need to check.

If the extent of tungsten contacts ablation is very serious, then: Firstly, put on gloves, remove the tungsten contacts, and put it on a flat stone; then, get some oil in your hand, then pull back and forth parallel to polish tungsten contacts, to prevent partial wear during, you should not use hand to swing it .

If the extent of tungsten contacts ablation is not serious, then: using platinum sand bar or fine sandpaper to smooth ablation. When using fine sandpaper, fine sandpaper can be turned over, so its sand finish is outwardly facing to polish tungsten contacts, and then be turned back, and erasing the dirt left by milling until tungsten contacts is clean.




Tungsten Metals Manufacturer & Supplier: Chinatungsten Online - http://www.tungsten.com.cn
 Tel.: 86 592 5129696; Fax: 86 592 5129797
 Email: sales@chinatungsten.com
 Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
 Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
 Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn

First of all, you should add appropriate proportion of nitric acid (8 mol / L) to scrapped silver tungsten points, and then heat them. You should filtrate after the above process, besides, the filtrate and scrubbing solution could be used together to prepare ultra-fine silver powder. Then, you should smash and sieve the residue after drying them.

Then, you should put the materials after first silver leaching process into the sintering furnace, and sinter 2h at a temperature of 500 ℃.

At last, you should wait until it cooling, and add nitric acid (8mol / L) to carry out secondary silver leaching, then cooling and filtering.




Tungsten Metals Manufacturer & Supplier: Chinatungsten Online - http://www.tungsten.com.cn
 Tel.: 86 592 5129696; Fax: 86 592 5129797
 Email: sales@chinatungsten.com
 Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
 Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
 Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn

Firstly, adding a certain amount of nitric acid (8 mol / L) to scrapped silver tungsten contacts, and then heating it. After that, filtration, and the filtrate and scrubbing solution can be used together for the preparation of ultra-fine silver powder. Then, smashing and sieving the residue after drying.

Secondly, put the materials after first silver leaching process into the sintering furnace, sintering 2h at a temperature of 500 ℃.

Finally, cooling, and adding nitric acid (8mol / L) to carry out secondary silver leaching, then cooling and filtering.




Tungsten Metals Manufacturer & Supplier: Chinatungsten Online - http://www.tungsten.com.cn
 Tel.: 86 592 5129696; Fax: 86 592 5129797
 Email: sales@chinatungsten.com
 Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
 Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
 Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn

If you electrify silver tungsten points for a short time, for one thing, the temperature of its contact surface will rise sharply, for another, because the current lines near the beam area is curved, it will appear the phenomenon of short-arc of silver tungsten points. The aforementioned conditions will melt silver tungsten points, and it will lead to silver tungsten points welding eventually. If the current used to energize silver tungsten points is near to the critical value of welding current, to some extent, silver tungsten points be welded. The material of silver tungsten points and its surface state will influence the welding resistance of silver tungsten points directly. In case of that there are surface film layers and uneven energized treatment, so you can reinforce the weld of silver tungsten points.

Silver tungsten points possess high welding force and welding strength. The initial welding current of silver tungsten points is around 1000A, and its maximum welding force is about 165N when the current is 0.9 peaks current; and silver tungsten points possess the largest welding strength of 750Pa around when the current is 4600A.




Tungsten Metals Manufacturer & Supplier: Chinatungsten Online - http://www.tungsten.com.cn
 Tel.: 86 592 5129696; Fax: 86 592 5129797
 Email: sales@chinatungsten.com
 Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
 Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
 Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn

If you energize silver tungsten contacts for a short time, on one hand, the temperature of its contact surface will be a sharp rise, on the other hand, it would make silver tungsten contacts short-arc because the current lines near the beam area is curved. The above two conditions will make the silver tungsten contacts melt, that is to say, it would lead to silver tungsten contacts welding. If the current through silver tungsten contacts is close to the critical value of welding current, silver tungsten contacts will be welded to some extent. The material of silver tungsten contacts and its surface state will directly affect the welding resistance properties of silver tungsten contacts. You can reinforce silver tungsten contacts’ welding in case of: there are surface film layers and uneven energized treatment.

Silver tungsten contacts materials have high welding force and welding strength. Silver tungsten contacts’ initial welding current is about 1000A, when the current is 0.9 peaks current, its maximum welding force is around 165N; when the current is 4600A, silver tungsten contacts have the largest welding strength of about 750Pa.




Tungsten Metals Manufacturer & Supplier: Chinatungsten Online - http://www.tungsten.com.cn
 Tel.: 86 592 5129696; Fax: 86 592 5129797
 Email: sales@chinatungsten.com
 Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
 Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
 Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn

2. Adding seed crystal and （NH₄）₂WO₄ solution.
During the first nucleary, adding seed crystal will obtain ammonium paratungstate which has largest Fsss grain size and apparent density. Adding complete seed crystal will obtain ideal even ammonium paratungstate. After the nucleary of ammonium paratungstate, adding （NH₄）₂WO₄ solution increase Fsss grain size and apparent density of ammonium paratungstate without changing distrubition of grain size. If the adding speed increases, micro ammonium paratungstate will be formed.

3.Mixture.
Increase the mixture speed, crystal formation rate is controlled by surface reaction instead of distribution. Ammonium paratungstate grain size varies in different mixture speed.

Tungsten Manufacturer & Supplier: Chinatungsten Online -http://www.tungsten-powder.com
Tel.: 86 592 5129696; Fax: 86 592 5129797
Email: sales@chinatungsten.com
Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn
 

Grain size of ammonium paratungstate affects the grain size of tungsten powder. Macro grain ammonium paratungstate has large apparent density and flow ability which promote the property and quality of tungsten powder. Marketing demand for macron ammonium paratungstate enlarges year by year. Macro grain ammonium paratungstate formation conditions include the influence of temperature, adding seed crystal and （NH₄）₂WO_4, the influence of mixture.

1.Temperature. Rapid heating up and reduce the degree of super saturation before boiling up. It will not only improve producing efficiency, also reduce the production rate of metatungstate radical A （HW₆O₂₁^5-）and the conversion rate of metatungstate radical A to metatungstate radical B（H₂W₁₂O₄₂^10-）.

Medium temperature nucleary. Reduce the formation of crystal nucleus. During nucleary of ammonium paratungstate, raise temperature in a certain degree will make the crystal grain size smaller.

Formation under high temperature. Reduce the rate of second nucleary. After the first nucleary, the distribution of ammonium paratungstate grain size depends on the second nucleary. After the first nucleary, heating up rapidly, reduce mixing time, thus reduce the second nucleary and crystal broken degree.


Tungsten Manufacturer & Supplier: Chinatungsten Online -http://www.tungsten-powder.com
Tel.: 86 592 5129696; Fax: 86 592 5129797
Email: sales@chinatungsten.com
Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn
 
 

Tungsten borides are compounds of tungsten and boron, and their most remarkable preoperty is high hardness. The Vickers hardness of tungsten borides or tungsten diboride is about 20GPa, and that of WB4 is about 30 GPa for loads exceeding 3 N. δ-WB and WB2 crystals have metallic resistivities of 0.1 and 0.3 mΩ·cm, respectively. The oxidation of W2B, WB and WB2 is significant at temperatures above 600 °C. The final oxidation products contain WO3 and probably amorphous B2O3 or H3BO3. The melting temnperatures of W2B, WB and WB2 are 2670, 2655 and 2365 °C, respectively.
WB2 has the same hexagonal structure as most diborides such as AlB2, MgB2 and it has several forms, α (tetragobal), β (orthorombic) and δ (tetragonal).
There are the ways for synthesis the tungsten borides.  Single crystals of WB2−x, x=0.07–0.17 (about 1 cm diameter, 6 cm length) were produced by the floating zone method, and WB4 crystals can be grown by arc-melting a mixture of elemental tungsten and boron.

Tungsten Manufacturer & Supplier: Chinatungsten Online -http://www.tungsten-powder.com
Tel.: 86 592 5129696; Fax: 86 592 5129797
Email: sales@chinatungsten.com
Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn