From Tungsten Electrode to GTAW Development Ⅱ

The following content is the other part of GTAW development on tungsten electrode.

Initially, the electrode overheated quickly and, despite tungsten's high melting temperature, particles of tungsten were transferred to the weld. To address this problem, the polarity of the electrode was changed from positive to negative, but the change made it unsuitable for welding many non-ferrous materials. Finally, the development of alternating current units made it possible to stabilize the arc and produce high quality aluminum and magnesium welds.

Developments continued during the following decades. Linde developed water-cooled torches that helped prevent overheating when welding with high currents. During the 1950s, as the process continued to gain popularity, some users turned to carbon dioxide as an alternative to the more expensive welding atmospheres consisting of argon and helium, but this proved unacceptable for welding aluminum and magnesium because it reduced weld quality, so it is rarely used with GTAW today. The use of any shielding gas containing an oxygen compound, such as carbon dioxide, quickly contaminates the tungsten electrode, making it unsuitable for the TIG process. In 1953, a new process based on GTAW was developed, called plasma arc welding. It affords greater control and improves weld quality by using a nozzle to focus the electric arc, but is largely limited to automated systems, whereas GTAW remains primarily a manual, hand-held method. Development within the GTAW process has continued as well, and today a number of variations exist. Among the most popular are the pulsed-current, manual programmed, hot-wire, dabber, and increased penetration GTAW methods. The following content is the other part of GTAW development on tungsten electrode.

The electrode overheated quickly initially and tungsten particles were transferred to the weld in spite of tungsten's high melting temperature. To deal with this problem, the electrode polarity was changed from positive to negative, but the change made it unsuitable for welding many non-ferrous materials. Finally, the development of alternating current units made it possible to stabilize the arc and produce high quality aluminum and magnesium welds.

Developments continued during the following decades. Linde developed water-cooled torches that helped prevent overheating when welding with high currents. During the 1950s, as the process continued to gain popularity, some users turned to carbon dioxide as an alternative to the more expensive welding atmospheres consisting of argon and helium, but this proved unacceptable for welding aluminum and magnesium because it reduced weld quality, so it is rarely used with GTAW today. The use of any shielding gas containing an oxygen compound, such as carbon dioxide, quickly contaminates the tungsten electrode, making it unsuitable for the TIG process. In 1953, a new process based on GTAW was developed, called plasma arc welding. It affords greater control and improves weld quality by using a nozzle to focus the electric arc, but is largely limited to automated systems, whereas GTAW remains primarily a manual, hand-held method. Development within the GTAW process has continued as well, and today a number of variations exist. Among the most popular are the pulsed-current, manual programmed, hot-wire, dabber, and increased penetration GTAW methods. 

Tungsten Metals Manufacturer & Supplier: Chinatungsten Online - http://www.tungsten.com.cn
 Tel.: 86 592 5129696; Fax: 86 592 5129797
 Email: sales@chinatungsten.com
 Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
 Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
 Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn

• < Prev
• Next >