Violet tungsten oxide with unique needle structure and high chemical activity has broad application prospects in the preparation of tungsten powder and tungsten carbide. Generally, it is obtained by calcining ammonium paratungstate in a calciner.

As a kind of multi-functional material, violet tungsten oxide has high application value in many fields such as fuel cells and thermal insulation materials. It is generally prepared by calcining ammonium paratungstate in a rotary furnace. The selection of rotary furnace is the key to high-quality violet tungsten oxide.

Violet tungsten oxide is an important raw material for the preparation of tungsten powder. During the preparation process, the fluidity of violet tungsten oxide directly determines the feeding speed of rotary furnace. Only when violet tungsten oxide with high fluidity is applied, can high-quality tungsten powder be prepared.

With high chemical activity and unique needle structure, violet tungsten oxide is an ideal raw material for preparing ultrafine tungsten powder. When applied in the production of tungsten powder, it can effectively improve the quality and performance of tungsten powder products.

Copper modified violet tungsten oxide is a kind of photocatalyst with good photocatalytic performance. As for its preparation, solution method is applied. This kind of preparation method is not only simple, but is suitable for large-scale production.

Violet tungsten oxide is a kind of photocatalyst with special surface structure and oxygen defect structure. In addition, copper can improve the response of the photocatalyst in the visible region. Therefore, copper modified violet tungsten oxide has broad application prospects in the field of photocatalyst.

With special surface structure and oxygen defect structure, violet tungsten oxide can be modified by copper ions, so as to have better photocatalytic properties. Copper modified violet tungsten oxide, which has a high rate of solar energy utilization, is an efficient photocatalyst.

Violet tungsten oxide is powder with unique color between dark purple and pure purple. It is generally prepared by calcining ammonium paratungstate in a rotary furnace. The color of violet tungsten oxide differs from different preparation methods.

In order to extract tungsten from tungsten minerals, at present, China's tungsten metallurgy industry mostly adopts the alkaline smelting system. After high-pressure leaching of sodium tungstate solution, ion exchange is carried out and apt is extracted by evaporation crystallization. At present, there are two outstanding problems in this process that have not been effectively solved: first, the waste water discharge is large. Second, the discharge of waste salt is large.

Among the many vanadium oxides, vanadium dioxide is different because of its rapid and sudden phase transition. Its phase transition temperature is 68 ℃, which can change reversibly from low temperature monoclinic system to high temperature tetragonal system, making its physical properties such as resistivity, optical transmittance and magnetic conductivity change greatly. This characteristic makes it have a great prospect in intelligent switch, electronic device and photoelectric equipment. The results show that tungsten can effectively reduce the phase transition temperature of vanadium dioxide, and copper can improve the conductivity of vanadium dioxide.