Ammonium Paratungstate Mechanochemical Decomposition

The possibility of mechanochemical decomposition of ammonium paratungstate (APT) has been studied, and compared with thermal decomposition method. For this purpose, APT powders were milled using a planetary ball mill up to 36 h and under air atmosphere. For thermal decomposition, APT powders were heated for 30 minutes at 300 and 450 °C in air atmosphere.

X-ray diffraction (XRD), differential scanning calorimeter (DSC), and thermo gravimetric analyzer (TGA) were used to study the decomposition progress, and products. The XRD results showed that APT completely decomposed to WO₃ by thermal decomposition, while the final product of mechanochemical decomposition was WO₃ (H₂O)_0.5. According to DSC and TGA results, during thermal decomposition, ammonia and water released in four steps, and leaved WO₃. By mechanochemical decomposition crystal water and ammonia liberated from APT structure, but structural water of APT remained. In both methods, an X-ray amorphous phase was the intermediate product of APT decomposition.




Tungsten Manufacturer & Supplier: Chinatungsten Online -http://www.tungsten-powder.com
Tel.: 86 592 5129696; Fax: 86 592 5129797
Email: sales@chinatungsten.com
Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn

• < Prev
• Next >