Partial thermal annealing of nominally pure calcium tungstate, after gamma irradiation at 78 °K, provided evidence for identifying three major 4900 Å thermoluminescence peaks at 0.36, 0.55, and 0.72 eV with three groups of electron spin resonance lines of paramagnetic tungsten at g₀₀₁ = 2.009 and 1.843 and niobium at g₀₀₁ = 2.021, respectively. The impurity center identified with the paramagnetic Nb⁺⁴ ion is assigned to a tungsten site and a NbOcomplex. Arguments are presented for the assignment of two lattice defect models, a WO complex with nearby WO₃ and NbO complexes, and a WO complex with a nearby calcium deficiency, to the paramagnetic (W⁺⁵)_A and (W⁺⁵)_B ions, respectively.

Teilweise Temperung von gamma-bestrahlten (78 °K), sogenannten reinen CaWO₄-Einkristallen ermöglichte die Identifizierung von drei ausgeprägten 4900 Å Thermolumineszenzmaxima bei 0,36, 0,55 und 0,72 eV mit drei Gruppen von ESR-Spektren, die mit paramagnetischem Wolfram mit g₀₀₁ = 2,009 und 1,843 bzw. Niobium mit g₀₀₁ = 2,021 verbunden sind. Die Fremdstörstelle wird als Nb⁺⁴ Ion auf Wolfram-Platz identifiziert und einem NbO-Komplex zugeordnet. Argumente für die Zuordnung der paramagnetischen (W⁺⁵)_A- bzw. (W⁺⁵)_B-Ionen zu zwei Eigenstörstellenmodellen, einem WO-Komplex mit benachbarten WO₃- und NbO-Komplexen und einem WO-Komplex mit einer benachbarten Kalzium-Fehlstelle, werden angeführt.