Ammonium Metatungstate Preparation-Thermal Decomposition Method

The thermal decomposition of ammonium paratungstate by preparing ammonium metatungstate: ammonium paratungstate and a small amount of citric acid catalyst after mixing into the far infrared, rotary furnace, controlled thermal decomposition temperature 200 ～ 280 ℃, decomposition of about 1 h. The removal of ammonia and water, ammonium paratungstate weightlessness rate was 5% ~ 6%.

The thermal decomposition products immediately after the slurry, adding proper amount of ammonia, Ph value is adjusted in the 3 to 4 range, at 90 ℃ digestion slurry. After evaporation to ammonium metatungstate content of 50% can be used as a liquid product to sell, crystallization, when the evaporation to the original volume of 20% filtering and separating, granulating product. Also can be evaporated and concentrated liquid product is prepared by spray drying. As of 45% ~ 50% ammonium metatungstate by high-speed centrifugal rotary spray dryer, imports of hot air temperature 250 ～ 300 ℃, outlet temperature 90 ～ 95 ℃, the obtained product is a spherical crystal, particle size is 200 mesh accounted for 95%, free water <1.5%.



Tungsten Manufacturer & Supplier: Chinatungsten Online -http://www.tungsten-powder.com
Tel.: 86 592 5129696; Fax: 86 592 5129797
Email: sales@chinatungsten.com
Tungsten & Molybdenum Information Bank: http://i.chinatungsten.com
Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
Molybdenum News & Molybdenum Price: http://news.molybdenum.com.cn

• < Prev
• Next >